Resistance to Impact : RESULTS 196kg.cm.

Test Method ASTM D2794
Height Level		Condition
	kg.cm	1	2	3	4	5
Low	192	Crack	No	No	No	No
Medium	196	No	Crack	No	No	Crack
High	200	No	Crack	No	Crack	Crack

Resistance to Fire : Simultaneous Determination of ignitability, Flame Propagation, Heat Release and Smoke Release.

Test Method AS 1530.31989 AMDT N01 Apr 92
Condition	Mean
Ignition Time	5.78 min
Flame Propagation Time	Nil secs
Heat Release Integral	71.1 kj/sq.M
Smoke Release, Log D	-0.8101
Optical Density, D	0.1572 /M

Test Method AS 1530.31989 AMDT N01 Apr 92
Condition	Mean	Index
Ignitability Index	14	0 - 2
Spread of Flame Index	0	0 -10
Heat Evolved Index	2	0 - 10
Smoke Developed Index	5	0 -10

Slip Resistance :

Test Method ASTM D4518
Condition	Result
Dry	0.53
Wet	0.50
Oiled	0.49
Oiled After Impact	0.41

Test Method DIN 51130
Grade	Result
Commercial	R -13
Industrial	R -12
Offshore	R -12

Test Method AS/NZ 3661.1
.	Commercial	Industrial	Offshore
Dry Leather	1.30	1.50	1.80
Dry Rubber	1.30	1.30	1.90
Wet Rubber	0.95	0.85	0.85

Resistance to Delamination : RESULTS 1.9 - 2.3 N/sq.mm. Test Method BS 3900 Pt. E10.

Resistance to Abrasion : Result > 313.6 g/mm. Test Method ASTM D658.

Chemical Resistance of Resins :

Javel Water (NaCl, Sodium hypochlorite)	14%
Sulphuric acid	10%
Nitric acid	30%
Formic acid	10%
Acetic acid	10%
Latic acid	5%
Petrol (tetraethyl lead fuel)
Toluene
Styrene
1.1, 1-trichloroethane
Skydrol 500A (hydraulic fluid for aircraft)
Test periods in week
		resistant slightly softened